6063 Aluminum Alloy CNC Machining Material Handbook
6063 Aluminum Alloy CNC Machining Material Handbook
Back to the CNC metal machining materials handbook
Material Quick Reference Card
┌──────────────────────────────────────────────┐
│ Material Name: 6063 Aluminum Alloy
│ Category: Al-Mg-Si heat-treatable aluminum alloy
│ Density: 2.70 g/cm³
│ Tensile Strength: 150–240 MPa
│ Yield Strength: 110–215 MPa
│ Hardness: 60–75 HB
│ Melting Point: 615–655 ℃
│ Machinability: ★★★★☆ Good
│ Corrosion Resistance: ★★★★★ Excellent
│ Cost: ★★★☆☆ Moderate
│ Keywords: extrusion, cosmetic parts, anodizing, profiles
└──────────────────────────────────────────────┘
1. Material Overview
1.1 Basic Introduction
6063 aluminum alloy is a 6-series aluminum alloy known for excellent extrudability, smooth surface quality, corrosion resistance, and stable anodizing results. It is widely used for decorative profiles, lightweight frames, housings, heat-sink profiles, and parts where appearance is more important than maximum strength.
In CNC machining, 6063 Aluminum Alloy should be evaluated by strength, stiffness, corrosion resistance, machinability, tolerance stability, surface treatment compatibility, cost, and production volume.
1.2 Source, Production, and Raw Stock Forms
Produced from refined aluminum alloyed mainly with magnesium and silicon. It is commonly supplied as extruded bar, tube, angle, channel, custom profile, sheet, and plate.
Common CNC raw material forms include round bar, square bar, plate, sheet, tube, extrusion, forging, casting, and custom blank. The best form depends on part geometry, required tolerance, mechanical properties, and order quantity.
2. Composition and Physical Properties
2.1 Chemical Composition and Grade System
| Element or Range | Typical Content | Function |
|---|---|---|
| Al | balance | Controls material performance |
| Mg | 0.45–0.90% | Controls material performance |
| Si | 0.20–0.60% | Controls material performance |
| Fe | ≤0.35% | Controls material performance |
| Cu | ≤0.10% | Controls material performance |
2.2 Physical Properties
| Property | Typical Value | CNC Relevance |
|---|---|---|
| Density | 2.70 g/cm³ | Affects part weight and handling |
| Melting point/range | 615–655 ℃ | Important for welding, heat treatment, and thermal safety |
| Thermal conductivity | Grade dependent | Affects cutting heat and heat dissipation |
| Electrical conductivity | Grade dependent | Important for electrical applications |
| Thermal expansion | Grade dependent | Affects precision and dimensional stability |
| Elastic modulus | Grade dependent | Affects rigidity and deflection |
3. Mechanical and Chemical Performance
3.1 Mechanical Properties
| Property | Typical Value |
|---|---|
| Tensile strength | 150–240 MPa |
| Yield strength | 110–215 MPa |
| Hardness | 60–75 HB |
| Elongation | Depends on grade, temper, and stock form |
| Fatigue strength | Application dependent and should be verified for critical parts |
Mechanical values vary with standard, heat treatment, product form, section thickness, and supplier certificate. For safety-critical parts, use certified material data instead of generic values.
3.2 Corrosion Resistance
Corrosion performance depends on alloy chemistry, environment, surface roughness, heat treatment, and protective finish. For outdoor, marine, chemical, medical, or high-humidity applications, confirm the required material grade and finishing process before machining.
3.3 Special Properties
Important special properties may include heat-treatment response, magnetic behavior, conductivity, weldability, high-temperature resistance, low-temperature toughness, biocompatibility, or environmental compliance. These should be reviewed according to the exact grade and application.
4. CNC Machining Process
4.1 Machinability Evaluation
Machinability rating: ★★★★☆ Good.
The machining strategy should consider material hardness, ductility, thermal conductivity, work-hardening tendency, chip shape, and tool wear behavior.
4.2 Recommended Tooling
Use rigid workholding, sharp tools, stable tool overhang, and suitable carbide tooling. For non-ferrous metals, polished flutes and high rake angles often improve chip evacuation. For steels, stainless steels, titanium, and nickel alloys, coating choice and coolant delivery are critical for tool life.
4.3 Reference Cutting Parameters
| Operation | Spindle Speed (RPM) | Feed Rate (mm/min) | Depth of Cut (mm) |
|---|---|---|---|
| Rough machining | Material and tool dependent | Material and tool dependent | Conservative first, then optimize |
| Finish machining | Higher but stable | Lower and consistent | 0.03–0.30 typical |
These values are starting references only. Final parameters should be adjusted according to tool diameter, machine rigidity, coolant, clamping, tolerance, and surface finish requirements.
4.4 Cooling and Lubrication
Use coolant strategy according to material behavior. Flood coolant is common for steels, stainless steels, titanium, and nickel alloys. Air blast or mist can be useful for aluminum and brass. Magnesium requires strict fire-safety controls for chips and dust.
4.5 Machining Challenges and Solutions
| Challenge | Recommended Solution |
|---|---|
| Tool wear | Use suitable coating, correct speed, stable coolant, and rigid setup |
| Burrs or long chips | Optimize rake angle, chip load, chip breaker, and finishing pass |
| Heat and distortion | Use staged machining, balanced stock removal, and stress-relieved material |
| Surface scratches | Control chip evacuation and handling |
4.6 Chip Control
Stable chip evacuation protects surface finish, improves tool life, and reduces dimensional variation. Chip form should be controlled by tool geometry, feed per tooth, depth of cut, coolant direction, and toolpath strategy.
5. Post-Processing and Finishing
5.1 Surface Treatment Options
Anodizing, sandblasting, brushing, powder coating, painting.
Typical CNC surface roughness can range from Ra 3.2 μm for general machining to Ra 0.8 μm or better with finishing passes, polishing, grinding, or lapping where applicable.
5.2 Heat Treatment
T5 and T6 are common. T5 is widely used after extrusion; T6 provides higher strength after solution treatment and aging.
6. Applications and Material Selection
6.1 Typical Applications
| Industry or Area | Typical Parts |
|---|---|
| Architecture | window frames and rails |
| Electronics | housings and heat sinks |
| Automation | frames and covers |
| Consumer goods | decorative aluminum parts |
6.2 Advantages and Limitations
| Advantages | Limitations |
|---|---|
| Excellent surface finish | Lower strength than 6061 and 7075 |
| Excellent anodizing | Soft before treatment |
| Good corrosion resistance | Burrs on thin edges |
| Easy extrusion |
6.3 Cost and Selection Advice
Relative material cost: ★★★☆☆ Moderate.
Choose 6063 Aluminum Alloy when its strength, corrosion resistance, machining behavior, surface finish, and cost match the part requirements. Compare it with nearby grades before final selection, especially when the design involves tight tolerance, harsh environment, heat treatment, welding, or high-volume production.